Genflam® CIC-3 BK thermoplastic flame retardant low smoke zero halogen compound was designed as a jacket for fire alarm cables that must meet the 2 hour fire endurance test UL 2196 at 1850 F. Groups of such cable must pass the IEEE 383 Cable Tray tests.

PRINCIPALES CARACTÉRISTIQUES

• High flame retardancy, no dripping
• Excellent processing
• No heavy metals or halogens

PROPRIÉTÉS PHYSIQUES

Densité : 1.58 g/cm3
Tension : 2000 psi (typical)
Élongation : 100% (typical)
Résistance à la déchirure : 21 lbf/in (typical)
Duromètre : 90 Shore A
Souplesse à basse température : Point de fragilité : ‐45ºC
Déformation, 2 000 g :  0%@121ºC   0%@100ºC   0%@90ºC

PROPRIÉTÉS ELECTRICAL

Dielectric Constant (DC): 3.53
Dissipation Factor (DF): 9.4 x 10^-3

PROPRIÉTÉS DE COMBUSTION

Indice limite d’oxygène (LOI) : 38%
Indice de fumée (norme ASTM E662) : 0.2%

VIEILLISSEMENT À LA CHALEUR

	7d@100ºC	7d@121ºC	10d@110ºC	30d@110ºC	70d@110ºC
Résistance à la traction	89%	107%	102%	TBD	TBD
Conservation de l’allongement	65%	68%	65%	TBD	TBD

RÉSISTANCE AUX FLUIDES

	IRM 902 – 4h@70ºC	Diesel – 24h@25ºC	IPA – 24h@23ºC
Résistance à la traction	95%	94%	94%
Conservation de l’allongement	97%	96%	88%

MÉTÉORISATION

	720 heures sous test QUV
Résistance à la traction	TBD
Conservation de l’allongement	TBD

CONDITIONS DE FONCTIONNEMENT SUGGÉRÉES

Extrusion (ratio L/D) : 20:1 or 25:1
Ratio comparatif : 1.25:1
Grillage : 20 Mesh or none
Type de vis : Single Flight metering, without mixing section
Zone d’introduction : 250ºF
Zone centrale : 300-320ºF
Tête/matrice : 350ºF
Préchauffage du conducteur : 165ºF
Die Cooling: 165ºF
Gradient Cooling: Not Recommended
Color Concentrate: Not Recommended

TECHNIQUES DE TRAITEMENT

Genflam CIC-3 Zero Halogen compound is designed to process easily, with a smooth extrudate.