Genflam® XL‐R CPE CV sheathing compound has been designed to process easily on standard extruders used in the production of wire and cable products. Genflam XL‐R CPE CV is supplied as free flowing pellets, packaged in sealed foil lined boxes and does not need to be dried prior to use.

KEY FEATURES

• Excellent flame performance
• Lead Free
• Excellent processing
• Oil Resistant

PHYSICAL PROPERTIES

Density: 1.42 g/cm³
Tensile: 2700 psi (uncured)
Elongation: 500% (uncured)
200% Modulus: 1100 psi (uncured)
Durometer: 98 Shore A
Low Temp. Brittle Point: ‐35ºC

COMBUSTION PROPERTIES

Limited Oxygen Index (LOI): 37% 

HEAT AGING

	7d@100ºC
Tensile Retention	88.65%
Elongation Retention	95.25%

FLUID RESISTANCE

	IRM 902 – 18h@121ºC
Tensile Retention	79.92%
Elongation Retention	86.16%

SUGGESTED RUNNING CONDITIONS

Extruder L/D: 20:1 or 25:1
Comp. Ratio: 1.25:1
Screen Pack: 20 Mesh or none
Screw Type: Single Flight metering, without mixing section
Feed Zone: 180ºF
Center Zone: 205-215ºF
Head/Die: 220ºF
Screw Cooling: 165ºF
Die Cooling: Not recommended
Gradient Cooling: Recommended
Color Concentrate: Not applicable

PROCESSING TECHNIQUES

Genflam XL‐R CPE CV sheathing compound has been designed to process easily on standard extruders used in the production of wire and cable products. This materials is designed to process similar to elastomeric compounds, attaining maximum output levels at relatively low shear rates. Care should be taken to ensure that screw compression ratio levels are below 1.5:1, and flow restrictions in the crosshead are kept to a minimum. Melt temperature values above 240ºF (115ºC) should be avoided.

The material can be extruded using either pressure or sleeving techniques. For generation of optimum physical properties, a draw down ratio of 1.25:1 can be used. Gradient cooling is also recommended for maximization of compound physical properties.

Genflam XL‐R CPE HP is supplied as free flowing pellets, packaged in sealed foil lined boxes and do not need to be dried prior to use. It is recommended that the foil liners be resealed after use to prevent outside contamination or moisture absorption during storage. If the material has been exposed to a high humidity environment, or the foil liner has not been sealed, it is recommended the material be dried for a minimum of 4 hours at 140ºF (60ºC) in a standard desiccant style dryer prior to use.