Genflam® XL‐R CPE sheathing compound has been designed with improved tear resistance to process easily on standard extruders used in the production of wire and cable products. Genflam XL‐R CPE is supplied as free flowing pellets, packaged in sealed foil lined boxes and does not need to be dried prior to use.
- Excellent flame performance
- Lead Free
- Excellent processing
- Oil Resistant
Density: 1.42 g/cm3
Tensile: 1520 psi (uncured) 2500 psi @ 12 MRads (typical)
Elongation: 680% (uncured) 350% @ 12 MRads (typical)
200% Modulus: 460 psi (uncured) 1150 psi @ 12 MRads (typical)
Durometer: 98 Shore A
Low Temp. Brittle Point: ‐35ºC
* Samples extruded as tape with a nominal thickness of 0.070 inches.
Limited Oxygen Index (LOI): 37%
|IRM 902 – 18h@121ºC|
SUGGESTED RUNNING CONDITIONS
Extruder L/D: 20:1 or 25:1
Comp. Ratio: 1.25:1
Screen Pack: 20 Mesh or none
Screw Type: Single Flight metering, without mixing section
Feed Zone: 200ºF
Center Zone: 225-240ºF
Screw Cooling: 165ºF
Die Cooling: Not recommended
Gradient Cooling: Recommended
Color Concentrate: Not applicable
Genflam XL‐R CPE HP sheathing compound has been designed to process easily on standard extruders used in the production of wire and cable products. This materials is designed to process similar to elastomeric compounds, attaining maximum output levels at relatively low shear rates. Care should be taken to ensure that screw compression ratio levels are below 1.5:1, and flow restrictions in the crosshead are kept to a minimum. Melt temperature values above 300oF (150oC) should be avoided.
The material can be extruded using either pressure or sleeving techniques. For generation of optimum physical properties, a draw down ratio of 1.25:1 can be used. Gradient cooling is also recommended for maximization of compound physical properties.
Genflam XL‐R CPE HP is supplied as free flowing pellets, packaged in sealed foil lined boxes and do not need to be dried prior to use. It is recommended that the foil liners be resealed after use to prevent outside contamination or moisture absorption during storage. If the material has been exposed to a high humidity environment, or the foil liner has not been sealed, it is recommended the material be dried for a minimum of 4 hours at 140oF (60oC) in a standard desiccant style dryer prior to use.
Similar products that might interest you
This fast Peroxide Curing Thermoset Flame Retardant Low Smoke Zero Halogen Compound was designed to provide the wire and cable field with a flame resistant jacketing compound.Learn More
Genfil TP BC
A zero halogen flame retardant cable bedding compound that was designed as a moisture proof barrier and filler for use in Low Smoke Halogen Free (LZHF) constructions.Learn More
GenNex EU Ins
This compound has been designed to process easily on standard extruders used in the production of wire and cable products. The material is supplied as free flowing pellets.Learn More